Product Specifications
| Features | Value | Measurement unit | Method |
| NCOcontent | 16.2?±0.4 | % | DIN EN ISO 11 909 |
| Viscosity@ 23℃ | 6,500?±1,500 | mPa?·s | DIN EN ISO 3219 |
| Hazencolor value?span> | ≤?150 | DIN EN 1557 | |
| isocyanate?monomer content | < 0.15 | %?(by weight) | DIN 55 956 |
Other Data*
| Features | Value | Measurement unit | Method |
| Density | about1.16 | g/cm3 | DIN 53 217 |
| Flashpoint | about230 | ℃ | DIN EN 53 213 |
Solubility/Dilution
Bayhydur 305 generally has good compatibility with organic solvents such as: esters, ether esters, xylene and solvent naphtha 100. However, in any case the solubility/miscibility of the prepared solution must be tested. Polyurethane grade solvents should be used (moisture content <0.05%)
Features/Applications
This product is a crosslinking agent for water-based paint. It is especially suitable for use in the civilian field where it can be mixed and used immediately after shaking or manual stirring.
Even in the pre-diluted condition, the coating film is still transparent and bright. The mixing ratio of mill base to curing agent is usually 10:1.
enter”>g/cm3
DIN 53 217
Flashpoint
about230
℃
DIN EN 53 213
Solubility/Dilution
Bayhydur 305 generally has good compatibility with organic solvents such as: esters, ether esters, xylene and solvent naphtha 100. However, in any case the solubility/miscibility of the prepared solution must be tested. Polyurethane grade solvents should be used (moisture content <0.05%)
Features/Applications
This product is a crosslinking agent for water-based paint. It is especially suitable for use in the civilian field where it can be mixed and used immediately after shaking or manual stirring.
Even in the pre-diluted condition, the coating film is still transparent and bright. The mixing ratio of mill base to curing agent is usually 10:1.